After reading the add, it says it is about 65 - 72% solids. I thought we are trying to find 100% solids w/ no VOC's?
<a href=showthread.php?s=&postid=14206493#post14206493 target=_blank>Originally posted</a> by apayne
MAS?
Fat-tony, what is MAS.
Also, what about using fiberglass resin. The type I have says after curing it has 0% VOC.
Thanks,
Aaron
If you are not sure it's inert, why would you use it when there are formulations that you can be sure of, since they are rated safe enough for people to store their drinking water in?<a href=showthread.php?s=&postid=14210867#post14210867 target=_blank>Originally posted</a> by apayne
So one more question, Can any two part epoxy work, or MUST it be approved for potable water. I would think once it has cured, it would be inert, but I am not sure.
Thanks,
Aaron